? supplier : samsung electro-mechanics ? samsung p/n : CL10B152KB85PNC ? product : multi-layer ceramic capacitor ? description : cap, 1.5 ? , 50v, 10%, x7r, 0603 ? aec-q 200 specified cl 10 b 152 k b 8 5 p n c ? ???? series samsung multi-layer ceramic capacitor size 0603 (inch code) l: 1.6 0.1 mm w: 0.1 mm dielectric x7r inner electrode ni , open mode capacitance 1.5 ? termination cu , ag-epoxy capacitance 10 % plating sn 100% (pb free) tolerance product automotive rated voltage 50 v grade code standard thickness 0.8 0.1 mm ? packaging cardboard type, 7" reel b. reliablility test and judgement condition high temperature unpowered, 1000hrs@t=150 exposure capacitance change : within 10% measurement at 242hrs after test conclusion tan : 0.03 max ir : more than 10,000 ? or 500 ? ? whichever is smaller temperature cycling 1000cycles capacitance change : within 10% measurement at 242hrs after test conclusion tan : 0.03 max 1 cycle condition : ir : more than 10,000 ? or 500 ? ? -55+0/-3 (153min) -> room temp(1min.) whichever is smaller -> 125+3/-0 (153min) -> room temp(1min.) destructive physical no defects or abnormalities per eia 469 analysis moisture resistance 10cycles, t=24hrs/cycle capacitance change : within 12.5% heat (25~65 ) and humidity (80~98%), unpowered tan : 0.03 max measurement at 242hrs after test conclusion ir : more than 10,000 ? or 500 ? ? whichever is smaller humidity bias 1000hrs 85 /85%rh, rated voltate and 1.3~1.5v, capacitance change : within 12.5% add 100kohm resistor tan : 0.035 max measurement at 242hrs after test conclusion ir : more than 500 ? or 25 ? ? the charge/discharge current is less than 50ma. whichever is smaller high temperature 1000hrs @ ta=125 , 200% rated voltage, operating life capacitance change : within 12.5% measurement at 242hrs after test conclusion tan : 0.035 max the charge/discharge current is less than 50ma. ir : more than 1000 ? or 50 ? ? whichever is smaller performance test condition appearance : no abnormal exterior appearance appearance : no abnormal exterior appearance appearance : no abnormal exterior appearance appearance : no abnormal exterior appearance 0.8 specification of automotive mlcc a. samsung part number appearance : no abnormal exterior appearance
external visual no abnormal exterior appearance microscope (10) physical dimensions within the specified dimensions using the calipers mechanical shock three shocks in each direction should be applied along capacitance change : within 10% 3 mutually perpendicular axes of the test specimen (18 shocks) tan , ir : initial spec. vibration 5g's for 20min., 12cycles each of 3 orientations, capacitance change : within 10% use 8"5" pcb 0.031" thick 7 secure points on one long side tan , ir : initial spec. and 2 secure points at corners of opposite sides. parts mounted within 2" from any secure point. test from 10~2000 ? . resistance to solder pot : 2605 , 101sec. solder heat capacitance change : within 10% tan , ir : initial spec. thermal shock -55 /+125 . capacitance change : within 10% note: number of cycles required-300, tan , ir : initial spec. maximum transfer time-20 sec, dwell time-15min. air-air esd aec-q200-002 capacitance change : within 10% tan , ir : initial spec. solderability 95% of the terminations is to be soldered a) preheat at 155 for 4 hours, immerse in solder for 5s at 2455 evenly and continuously b) steam aging for 8 hours, immerse in solder for 5s at 2455 c) steam aging for 8 hours, immerse in solder for 120s at 2605 solder : a solution ethanol and rosin electrical capacitance : within specified tolerance the capacitance /d.f. should be measured at 25 , characterization tan (df) : 0.025 max. 1 ? 10%, 1.00.2vrms ir(25 ) : more than 10,000 ? or 500 ? ? i.r. should be measured with a dc voltage not exceeding ir(125 ) : more than1,000 ? or 10 ? ? rated voltage @25 , @125 for 60~120 sec. whichever is smaller dielectric strength dielectric strength : 250% of the rated voltage for 1~5 seconds board flex bending to the limit (2 L ) for 5 seconds capacitance change : within 10% terminal 10n, for 601 sec. strength(smd) capacitance change : within 10% beam load destruction value should not be exceed beam speed chip length < 2.5 L 0.50.05 L /sec a) chip thickness > 0.5 L : 20n b) chip thickness 0.5 L : 8n temperature x7r characterisitcs (from -55 to 125 , capacitance change shoud be within 15%) c. recommended soldering method : reflow ( reflow peak temperature : 260+0/-5 , 10sec. max ) meet ipc/jedec j-std-020 d standard * for the more detail specification, please refer to the samsung mlcc catalogue. velocity performance test condition appearance : no abnormal exterior appearance appearance : no abnormal exterior appearance duration wave appearance : no abnormal exterior appearance appearance : no abnormal exterior appearance appearance : no abnormal exterior appearance 1,500g peakvalue appearance : no abnormal exterior appearance 0.5ms half sine 4.7m/sec. appearance : no abnormal exterior appearance
|