d a t a sh eet product specification supersedes data of 24th may 2000 2001 may 30 rev.5 discrete ceramics class 2, x7r 10 v surface-mount ceramic multilayer capacitors www.phycomp-components.com
2001 may 30 rev.5 2 www.phycomp-components.com phycomp product specification surface-mount ceramic multilayer capacitors class 2, x7r 10 v features ? three standard sizes ? for high frequency applications ? supplied in tape on reel or in bulk case ? nisn terminations. applications consumer electronics, for example: ? tuners ? television receivers ? video recorders ? all types of cameras. description the capacitor consists of a rectangular block of ceramic dielectric in which a number of interleaved metal electrodes are contained. this structure gives rise to a high capacitance per unit volume. the inner electrodes are connected to the two terminations and finally covered with a layer of plated tin (nisn). a cross section of the structure is shown in fig.1. quick reference data note 1. measured at 20 c, 1 v and 1 khz, using a four-gauge method. description value rated voltage u r (dc) 10 v capacitance range (e6 series) 150 nf to 2.2 f; note 1 tolerance on capacitance after 1000 hours 10% test voltage (dc) for 1 minute 2.5 u r sectional specifications iec 60384-10, second edition 1989-04; also based on cecc 32 100 detailed specification based on cecc 32 101-801 end terminations nisn climatic category (iec 60068) 55/125/21 fig.1 construction of a ceramic multilayer capacitor. mlb457 terminations electrodes ceramic material
2001 may 30 rev.5 3 www.phycomp-components.com phycomp product specification surface-mount ceramic multilayer capacitors class 2, x7r 10 v mechanical data physical dimensions table 1 capacitor dimensions; see fig.2 case size l 1 w tl 2 and l 3 l 4 min. min. max. min. max. dimensions in millimetres 0603 1.6 0.10 0.8 0.07 0.73 0.87 0.25 0.65 0.40 0805 2.0 0.10 1.25 0.10 0.50 1.35 0.25 0.75 0.55 1206 3.2 0.15 1.6 0.15 0.50 1.75 0.25 0.75 1.40 dimensions in inches 0603 0.063 0.004 0.032 0.003 0.029 0.035 0.010 0.026 0.016 1206 0.126 0.006 0.063 0.006 0.020 0.069 0.010 0.030 0.056 0805 0.079 0.004 0.049 0.004 0.020 0.053 0.010 0.030 0.022 fig.2 component outline. mbb211 t l 4 l 1 l 2 l 3 w for dimensions see table 1.
2001 may 30 rev.5 4 www.phycomp-components.com phycomp product specification surface-mount ceramic multilayer capacitors class 2, x7r 10 v selection chart thickness classification and packing quantities c (nf) last two digits of 12nc 10 v 0603 0805 1206 150 52 180 53 0.80 0.07 220 54 0.6 0.10 270 55 330 56 390 57 0.85 0.10 470 58 560 59 680 61 1.25 0.10 820 62 values in shaded cells indicate thickness classification. 1 000 63 0.85 0.10 1 200 64 1 500 65 1 800 66 1.15 0.10 2 200 67 thickness classification (mm) 8mm tape width quantity per reel quantity per bulk case ? 180 mm; 7" ? 330 mm; 13" 0603 0805 paper blister paper blister 0.6 0.10 4 000 ? 20 000 ??? 0.80 0.07 4000 ? 15 000 ? 15 000 ? 0.85 0.10 4000 ? 15 000 ??? 1.15 0.10 ? 3000 ? 10 000 ?? 1.25 0.10 ? 3000 ? 10 000 ? 5000
2001 may 30 rev.5 5 www.phycomp-components.com phycomp product specification surface-mount ceramic multilayer capacitors class 2, x7r 10 v ordering information components may be ordered by using either a simple 15-digit clear text code or phycomp?s unique 12nc. clear text code example: 06032r154k6bb0d size code temp. char. capacitance tol. voltage termination packing marking series 0603 0805 1206 2r = x7r 154 = 1 50 000 pf; the third digit signifies the multiplying factor: 4= 10 000 5= 100 000 k= 10% 6 = 10 v b = nisn 2 = 180 mm; 7 " paper 3 = 330 mm; 13 " paper b = 180 mm; 7 " blister f = 330 mm; 13" blister p = bulk case 0 = no marking d = bme ordering code 12nc (1) refer to chapter ?selection chart?. (2) quantity on reel depends on thickness classification, see section ?thickness classification and packing quantities?. handbook, full pagewidth 2 2 x x x x x x 5 x x x carrier type 22 38 54 blister paper tape bulk rated voltage - termination 24 10 v; nisn size 6 0 1 0603 0805 1206 capacitance value (1) tolerance 6 10% packaging (2) 1 5 4 reel: ? 180 mm; 7" reel: ? 330 mm; 13" bulk case ccb409
2001 may 30 rev.5 6 www.phycomp-components.com phycomp product specification surface-mount ceramic multilayer capacitors class 2, x7r 10 v electrical characteristics class 2 capacitors; x7r dielectric; nisn terminations unless otherwise stated all electrical values apply at an ambient temperature of 20 1 c, an atmospheric pressure of 86 to 105 kpa, and a relative humidity of 63 to 67%. note 1. measured at 20 c, 1 v and 1 khz, using a four-gauge method. description value capacitance range (e6 series); note 1 150 nf to 2.2 f tolerance on capacitance after 1000 hours 10% tan ; note 1 5% insulation resistance after 1 minute at u r (dc) r ins c 500 seconds maximum capacitance change as a function of temperature 15% ageing typical 3% per time decade resistance to soldering heat 260 c; 10 seconds
2001 may 30 rev.5 7 www.phycomp-components.com phycomp product specification surface-mount ceramic multilayer capacitors class 2, x7r 10 v tests and requirements table 2 test procedures and requirements iec 60384-10/ cecc 32 100 clause iec 60068-2 test method test procedure requirements 4.4 mounting the capacitors may be mounted on printed-circuit boards or ceramic substrates by applying wave soldering, reflow soldering (including vapour phase soldering) or conductive adhesive no visible damage 4.5 visual inspection and dimension check any applicable method using 10 magnification in accordance with specification 4.6.1 capacitance f = 1 khz; measuring voltage 1v rms at 20 c within specified tolerance 4.6.2 tan f = 1 khz; measuring voltage 1v rms at 20 c in accordance with specification 4.6.3 insulation resistance at u r (dc) for 1 minute in accordance with specification 4.6.4 voltage proof 2.5 u r for 1 minute no breakdown or flashover 4.7.1 temperature characteristic between minimum and maximum temperature in accordance with specification 4.8 adhesion a force of 5 n applied for 10 s to the line joining the terminations and in a plane parallel to the substrate no visible damage 4.9 bond strength of plating on end face mounted in accordance with cecc 32 100, paragraph 4.4 no visible damage conditions: bending 1 mm at a rate of 1 mm/s, radius jig 340 mm ? c/c: 10% 4.10 tb resistance to soldering heat precondition: 120 to 150 c for 1 minute; 260 5 c for 10 0.5 s the terminations shall be well tinned after recovery ? c/c: 10% resistance to leaching 260 5 c for 30 1s in a static solder bath using visual enlargement of 10, dissolution of the terminations shall not exceed 10% 4.11 ta solderability zero hour test, and test after storage (20 to 24 months) in original packing in normal atmosphere; unmounted chips completely immersed for 2 0.5 s in a solder bath at 235 5 c the terminations shall be well tinned
2001 may 30 rev.5 8 www.phycomp-components.com phycomp product specification surface-mount ceramic multilayer capacitors class 2, x7r 10 v 4.12 na rapid change of temperature preconditioning; 5 cycles in the following sequence: 30 minutes at ? 55 c, change within 30 minutes to + 125 c no visible damage after 48 hours recovery: ? c/c: 15% 4.14 ca damp heat, steady state initialization: 48 hours after u r at 40 c for 1 hour (for initial value measurement); 500 12 hours at 40 c; 90 to 95% rh; u r applied preconditioning: u r at 40 c for 1 hour after 48 hours recovery: ? c/c: 15% tan :7% r ins : 500 m ? or r i c r 25 s, whichever is less 4.15 endurance initialization: 2 u r at 125 c for 1 hour (initial value is measured after 48 hours, recovery at room temperature); 1000 hours at 125 c and 2 u r applied after 48 hours recovery: ? c/c: 20% tan :7% r ins : 1000 m ? or r i c r 50 s, whichever is less iec 60384-10/ cecc 32 100 clause iec 60068-2 test method test procedure requirements
2001 may 30 rev.5 9 www.phycomp-components.com phycomp product specification surface-mount ceramic multilayer capacitors class 2, x7r 10 v revision history revision date change notification description rev.5 2001 may 30 ? - converted to phycomp brand
|